ISO16925涂料和清漆. 涂層耐壓力水噴射測(cè)試
1 Scope
This International Standard specifies a test method for the assessment of the resistance of coatings to
pressure water-jetting. The test method simulates the effects pressure water-jetting has on a coating.
5 Apparatus ａnd materials
Ordinary laboratory apparatus, together with the following:
5.1 Pressure water-jet, consisting of a high-pressure pump ａnd a nozzle.
A high-pressure pump conveys the water from a storage bin. To avoid influences from variations in
pressure, it is necessary that the pressure ａnd the volumetric flow rate be adjustable at the nozzle
described below.
The water temperature shall be adjustable to ± 2 °C.
The temperature shall be adjusted in accordance withAnnex A. Necessary safety devices on the pressure
side of the unit, as e.g. pressure relief valve ａnd by-pass valve, shall exist. If the jetting is unsteady, a flow
calming section may be installed in front of the nozzle. A pulsation of the water jet at the opening of the
pump is inadmissible. In order to reach a reproducible result, the nozzle shall be solidly mechanically
fixed ａnd the test specimen shall be secured against slipping. For the adjustment of the volumetric flow
rate, a nozzle with a jet angle of 25° ａnd a volumetric flow rate of 6 l/min at 2 MPa (20 bar) is required
(seeAnnex A).
The following technical data should be attainable:
— volumetric flow rate: 8 l/min to 14 l/min
— pressure: 4 MPa (40 bar) to 13 MPa (130 bar)
— temperature: 20 °C to 80 °C
— jetting time: 10 s to 300 s

Figure 1 shows the schematic construction of a pressure water-jet apparatus which is specially built forthese tests.
 
Key
1 flow calming section
2 high-pressure valve, height adjustable
3 test specimen
4 clamping element  
5 feed tank
6 floating valve with filter
7 water shortage safeguard
8 heating
9 base frame, moveable
10 temperature sensor 
11 high-pressure pump
12 by-pass valve  
13 pressure relief valve
14 pressure transmitter
8.1 Introducing the cut or the scribe
Make sure that the test specimen is securely fastened when introducing the cut or the scribe.
Introduce both of the cuts or scribes vertically through the coating into the substrate using the cutting
or scribing tool, as shown inFigure 2. The depth of the cut or scribe into the substrate should be as
minimal as possible. The length of the first cut or scribe shall be at least 100 mm, if the geometry of the
part allows that. At an angle, introduce a second cut or scribe with a minimum length of 20 mm. The
cuts or scribes shall be introduced straight-line at an angle of approximately 30°. An automatic cutting
or scribing device may be used. Residues of the coating shall be removed from the cut or scribe.
NOTE The depth of the cut or scribe into the substrate influences the result.
The cutting or scribing tools should be checked regularly ａnd replaced if necessary.

   Figure 2 — Introducing the cuts or scribes (St Andrew’s cross)

8.2 Testing
After inserting the test specimen into the apparatus (e.g. using a spacer block), calibrate the space
between test specimen ａnd nozzle.
Operate the pressure water-jetting apparatus at room temperature.
Three test methods (A, B, or C – seeTable 1) are preferred as well as three possible scribing tools (C, L, or
S – see5.3). The test method to be applied, the scribing or cutting tool to be used, ａnd the water pressure
shall be agreed.
Table 1 — Test methods

 
For jetting, deionized water should be used.
When using automatic ａnd manual devices, fasten the test specimen so that the water jet impacts as
shown inFigure 3. The jet impacts in the middle above the point of intersection onto the longer one of both cuts/scribes.

Figure 3 — Jetting area

9Evaluation
9.1 General
Damage is recognizable when the coating loosens or flakes, regardless of which coat sustains the damage.
9.2 Evaluation with pictures to compare
Carry out the evaluation visually, comparing the specimen with the pictures.
In the course of the visual evaluation, a characteristic value is laid down by comparing with the
illustrations inFigures 4 to9. A characteristic value between 1 ａnd 5 results, depending on the degree
of damage. No damage corresponds to the characteristic value 0. In addition to the evaluation, if
applicable, the attribution of the separation from the main separation level or to the respective film
shall be indicated.
The result of the visual assessment is indicated in dependence of the applied method, for example:
— method A: characteristic value A;
— method B: characteristic value B;
— method C: characteristic value C.
NOTE In addition, by measuring the areas of flaking (maximum width, in millimetres, or area, in square
millimetres), the overall damage can be evaluated. The overall damage is calculated by summing up all damaged
areas of the test specimen. Even the smallest areas of flaking are measured ａnd calculated, ａnd all areas added to
the overall damage.

Figure 5 — Characteristic value 1 for pressure water-jet damage

Figure 6 — Characteristic value 2 for pressure water-jet damage


Figure 7 — Characteristic value 3 for pressure water-jet damage

Figure 8 — Characteristic value 4 for pressure water-jet damage

Figure 9 — Characteristic value 5 for pressure water-jet damage

 
Annex A
(normative)
Calibration of the test apparatus
A.1 Apparatus ａnd materials
Ordinary laboratory apparatus, as well as the following.
A.1.1 Temperature measuring device, with sensor, capable of measuring to 0,5 °C.
A.1.2 Balance, weighing to 10 g.
A.1.3 Time measuring device (swatch), capable of measuring ± 0,1 s.
A.1.4 Container, for the determination of the volumetric flow rate for at least 20 l of water.
A.1.5 Plastic block, made of polystyrene rigid plastic foam.
The kind of the polystyrene rigid plastic foam shall be agreed by the interested parties.
A.1.6 Length measuring device, capable of measuring ± 0,1 mm.
A.2.4 Calibration of the water jet
The conditions for the calibration of the jetting are in accordance with method B. For the calibration of
the jetting, a stainless steel precision flat film extrusion die with a volumetric flow rate of the nozzle of
6 l/min at 2 MPa (20 bar) ａnd a jet angle 25° is used. This nozzle is required to produce an even liquid
distribution during the entire jetting.
When using an automatic pressure-water apparatus, fasten the polystyrene rigid plastic foam in the
apparatus so that the jet cannot move the block. When using a manual apparatus, fasten the block in a
similar fixture.
After jetting, the length ａnd the width of the impact are measured. SeeFigure A.1.
The mean length of the impact shall be (73 ± 5) mm ａnd the mean width (8 ± 1) mm on average.


Figure A.1 — Measures of the washed-out areas in the polystyrene rigid plastic foam

蒸汽噴射試驗(yàn)機(jī)滿足測(cè)試規(guī)范汽車(chē)廠家：寶馬、奔馳、通用、大眾、福特、沃爾沃等規(guī)范（AA-0136、DIN 55662、ISO16925，DBL 7381，GM9531P、PV1503、VOLVO STD 423-0015，VOLVOVCS 1029 54719、FLTMBO 160-04、MS210-07，PSA D23 5376，Renault D25 2018/-A-2001，GMW16745-2012方法B，TPJLR-52.561-2009） 

上海鼎振儀器設(shè)備有限公司（簡(jiǎn)稱(chēng)“鼎徵設(shè)備”），位于上海市。是一家銷(xiāo)售檢測(cè)設(shè)備的廠家。主要代理銷(xiāo)售進(jìn)口： 循環(huán)鹽霧試驗(yàn)箱、氙燈老化試驗(yàn)機(jī)、高低溫試驗(yàn)機(jī)、金相顯微鏡、耐磨試驗(yàn)機(jī)、光澤度計(jì)，色差儀，超聲波探傷儀、超聲波測(cè)厚儀、涂層測(cè)厚儀、便攜式硬度計(jì)、電火花檢測(cè)儀、金屬電導(dǎo)率儀、鐵素體檢測(cè)儀等檢測(cè)設(shè)備。

合作品牌：
美國(guó)Taber，德國(guó)Erichsen，德國(guó)BYK，德國(guó)Liebisch，德國(guó)Fischer，德國(guó)Walter，德國(guó)ZEISS，德國(guó)Belce，
德國(guó)EPK，OLYMPUS 

公司一貫堅(jiān)持“質(zhì)量為本，用戶至上，優(yōu)質(zhì)服務(wù)，信守合同”的宗旨，憑借著高質(zhì)量的產(chǎn)品，良好的信譽(yù)，優(yōu)質(zhì)的服務(wù)。竭誠(chéng)與國(guó)內(nèi)外商家雙贏合作，共同發(fā)展，共創(chuàng)輝煌！